FWF Project - Thermomechanical Welding (TMW)

TMW experimental setup
© IMAT/TU Graz

All metallic materials consist of grains which are just a few hundredths of a millimeter. Alloys with finer grains usually have higher strength and toughness in comparison to materials with coarser grains. Therefore, the grain refinement leads to weight decrease of components which is associated with economic and ecological benefits. Among the grain refinement processes, thermo-mechanically controlled processes (TMCP) are the most efficient technique for the majority of alloys. During a TMCP, metals are subjected to plastic deformation which leads to deformed grains with high stored energy supporting the nucleation of new grains in further treatments at high temperatures (Recrystallization). The grains are usually prone to coarsening at high temperatures what is called grain growth. To inhibit the coarsening of the recrystallized grains, TMCP is associated with an accelerated cooling process subsequently after recrystallization. Alloys subjected to a welding process can experience grain growth due to the exposure to high temperatures. Thus, the deterioration of the strength and toughness of the welded material cannot be avoided. Various techniques like welding arc pulsation, electromagnetic and ultrasonic weld-pool stirring have been proposed in the literature to refine grains during welding. However, these techniques are restricted to specific welding conditions and alloy compositions, and are exclusively applicable to the molten weld metal (WM). However, besides the WM, grain growth occurs also in the adjacent area of the WM which is called heat affected zone (HAZ). This project proposes Thermo-Mechanical Welding (TMW), comparable to TMCP, and targets on refining the grain size in both the WM and HAZ regions. To estimate the appropriate time for deformation and appropriate cooling rate, a fundamental investigation of thermodynamics, kinetics, and mechanisms of the grain growth and recrystallization is required. Accordingly, comprehensive modeling will be performed comprising FEM, analytical simulation and cellular automata (CA). In parallel, physical simulation using the thermomechanical GLEEBLE system and validation experiments with the versatile TMW machine, which was constructed by the applicant, are envisaged. Within the proposed project two types of steels representing high strength low alloyed steel (HSLA) and austenitic stainless steel will be investigated. Also, along with the ex-situ metallographic techniques, a new in-situ technique, so-called LUMet, will be used to measure the grain size and kinetics of recrystallization within cooperation with the University of British Columbia. The innovation of the project lies in a new combined deterministic and probabilistic CA method to simulate grain growth and recrystallization and also the introduction of a comprehensive grain refinement method for the welding process. Improvement of the welding joint microstructures via TMW would yield to an improvement of the properties (strength, toughness) and Non-destructive test capability of the weldment.

Funding
image/svg+xml
Cooperation
image/svg+xml
Projectteam
image/svg+xml

Projectleader:
Assoc. Prof. Dipl.-Ing. Dr.techn. Norbert Enzinger
norbert.enzingernoSpam@tugraz.at
phone: +43 316 873 7182
 

Mohammad Bagher Nasiri, Fogh-lis.
mohammad.nasiri@tugraz.at
phone: +43 316 873 1672

Univ.-Prof. Dipl.-Ing. Dr.techn. Christof Sommitsch
christof.sommitschnoSpam@tugraz.at
phone: +43 316 873 7180

Assoc.Prof. Dr.techn. Cecilia Poletti
cecilia.polettinoSpam@tugraz.at
phone +43 316 873 1676

Dipl.-Ing. Dr.techn. Rudolf Vallant
rudolf.vallantnoSpam@tugraz.at
phone +43 316 873 1661